Research on the refinement mechanism of primary silicon particles on the basis of AlSi21CuNi alloy
PL Badania mechanizmu rozdrabniania pierwotnych kryształów krzemu na przykładzie stopu AlSi21CuNi
2014
artykuł naukowy
angielski
- hypereutectic silumin
- modification mechanism
- primary Si crystals
- silumin nadeutektyczny
- mechanizm modyfikacji
- pierwotne kryształy krzemu
EN A modification technology of hypereutectic Al-Si alloys has been known for many years. However, there are divergences among the scholars relating to interpreting the mechanism of phosphorus influence on refinement of the primary silicon particles. This article contributes to confirm the hypothesis of a heterogeneous influence of phosphorus in the process of crystallization of the primary silicon in hypereutectic Al-Si alloys. The existence of particle phases in the microstructure of AlSi21CuNi alloy, which may constitute heterogeneous crystallization centers in the precipitation process in primary silicon, has been proved by the methods of scanning microscopy and EDS microanalysis, as well as line analysis.
PL Technologia modyfikacji siluminów nadeutektyczych jest znana od wielu lat, jednakże badacze różnie interpretują mechanizm oddziaływania fosforu podczas rozdrabniania pierwotnych kryształów krzemu. Niniejszy artykuł stanowi przyczynek do potwierdzenia hipotezy o heterogenicznym oddziaływaniu fosforu w procesie krystalizacji pierwotnych wydzieleń krzemu w siluminach nadeutektycznych. Metodami mikroskopii skaningowej i mikroanalizy EDS oraz analizy liniowej udokumentowano występowanie w mikrostrukturze siluminu AlSi21CuNi cząstek fazy AlP mogących stanowić ośrodki heterogenicznej krystalizacji w wydzieleniach pierwotnego krzemu.