Micro Arc Oxidation of Mechanically Alloyed Binary Zn-1X (X = Mg or Sr) Alloys
[ 1 ] Instytut Inżynierii Materiałowej, Wydział Inżynierii Materiałowej i Fizyki Technicznej, Politechnika Poznańska | [ P ] employee | [ S ] student
2023
scientific article
english
- zinc alloys
- mechanical alloying
- anodic oxidation
- corrosion
- surface energy
EN The binary Zn-1wt.% X (X = Mg or Sr) alloys prepared by the application of mechanical alloying (MA) combined with powder metallurgy were modified by micro-arc oxidation (MAO) treatment in the 2 g/dm3 KOH aqueous solution at 200 V for 1 min for the formation of the ZnO layer. The Zn-alloys, obtained through the powder metallurgy method, are characterized by a dispersive microstructure that significantly improves its microhardness up to 90.5 HV0.3 for the Zn-1wt.%Mg sample after 24 h of MA. In the case of Zn-1Mg alloy after 24 h of mechanical alloying, Zn-1Mg alloy after 48 h of mechanical alloying, and Zn-1Sr alloy after 48 h of mechanical alloying, except for the main αZn phase, the traces of a second phase are noticed: MgZn2 and SrZn13. After the proposed MAO treatment, a zinc oxide (ZnO) layer on the zinc alloys was formed, allowing a significant improvement in the corrosion resistance and surface wetting properties. The potential of the modified ZnO layer is moved to more noble values in the case of MAO-treated samples α-Zn, Zn-1Mg (after 24 h of MA), and Zn-1Sr (after 48 h of MA). The obtained results show a good prospective potential of Zn-1wt.% X (X = Mg or Sr) binary alloys in the application of biodegradable materials.
16.10.2023
1503-1 - 1503-14
Article number: 1503
CC BY (attribution alone)
open journal
final published version
at the time of publication
70
2,7 [List 2022]