Efekty zastąpienia cementu portlandzkiego cementem glinowo-wapniowym w utworzonych przez nie zaczynach i zaprawach

Authors

[ 1 ] Instytut Budownictwa, Wydział Inżynierii Lądowej i Transportu, Politechnika Poznańska | [ P ] employee

Scientific discipline (Law 2.0)

[2.7] Civil engineering, geodesy and transport

Title variant

EN Effect of replacing Portland cement with alumina-lime cement in the slurries and mortars formed by them

Year of publication

2022

Published in

Materiały Budowlane

Journal year: 2022 | Journal number: nr 7

Article type

scientific article

Publication language

polish

Keywords
PL
  • cement glinowo-wapniowy
  • wiązanie natychmiastowe
  • adhezja
  • wytrzymałość na ściskanie
EN
  • alumina-lime cement
  • immediate setting
  • adhesion
  • compressive strength
Abstract

PL Celem badań było określenie wpływu, jaki ma zastosowanie cementu portlandzkiego z dodatkiem różnych odmian cementu glinowo-wapniowego na podstawowe cechy fizykomechaniczne zaczynów i zapraw. Do badań użyto CEM I 42,5R oraz trzech odmian cementu glinowego zawierającego 40, 50 i 70% Al2O3. Wykonano zaczyny z zawartością 4, 6, 8, 10 i 12% różnych odmian cementu glinowego i określono czas początku i końca wiązania. Na podstawie uzyskanych wyników badań ustalono optymalną proporcję cementu portlandzkiego do cementu glinowego i przy tej proporcji wykonano badania wytrzymałości na ściskanie zapraw wykonanych przy ich użyciu po 1, 2, 7 i 28 dniach dojrzewania oraz określono siłę adhezji do podłoża betonowego. Analiza uzyskanych wyników badań wykazała, że stosując dodatek 6%cementu wysokoglinowego, można uzyskać podobny efekt wiązania natychmiastowego i wyraźnie lepszą siłę adhezji jak z zastosowaniem 12% cementu niskoglinowego.

EN The aim of the research was to determine the influence of the use of Portland cement with the addition of various types of aluminum cement on the basic physical and mechanical properties of grouts and mortars. CEM I 42.5R and three types of aluminum cement containing 40, 50 and 70% Al 2 O 3 were used for the tests. Mixtures were made containing 4, 6, 8, 10 and 12% of different grades of alumina cement. The time of the beginning and the end of the bonding was determined for them. Based on the obtained research results, the optimal proportion of Portland cement to alumina cement was established. For this proportion, the compressive strength tests were carried out after 1, 2, 7 and 28 days of maturation of the mortars made with them, and the strength of their adhesion to the concrete substrate was determined. The analysis of the obtained test results showed that by using the addition of 6% high-alumina cement, a similar immediate setting effect can be obtained and a clearly better adhesive strength as when using 12% low-alumina cement.

Pages (from - to)

46 - 48

DOI

10.15199/33.2022.07.09

URL

https://www.materialybudowlane.info.pl/pl/14335

Open Access Mode

publisher's website

Open Access Text Version

final published version

Ministry points / journal

100

This website uses cookies to remember the authenticated session of the user. For more information, read about Cookies and Privacy Policy.