Influence of hydrogen on a nanocrystalline high-entropy oxide with application potential in hydrogen technologies
[ 1 ] Instytut Inżynierii Materiałowej, Wydział Inżynierii Materiałowej i Fizyki Technicznej, Politechnika Poznańska | [ P ] employee
2023
scientific article
english
- hydrogen
- high-entropy oxide
- nanocrystalline materials
- mechanical synthesis
EN The influence of hydrogen on a (Co0·2Cu0·2Mg0·2Ni0·2Zn0.2)O HEO with a rock salt structure was studied. Two forms of this HEO (nanopowder and sinter) were prepared via mechanochemical synthesis (MS) and additional heat treatment, respectively. The chemical stability of the synthesized samples in a pure hydrogen atmosphere was investigated using Sievert's technique. High-pressure hydrogenation at 250 °C had no noticeable effect on the HEO sinter. The sintered sample was chemically, structurally, and morphologically stable, as confirmed via the XRD, Raman spectroscopy, SEM, and XPS techniques. Thermogravimetric analysis (TGA) showed the sinter to be stable in an argon gas mixture with 5 vol% of hydrogen and over the temperature range of up to 400 °C.
19.01.2023
15544 - 15552
100
5,1